Materials & Coatings

This technology is well suited for environments requiring insulation materials that can withstand temperatures of up to 1200 °C.

NASA’s Glenn Research Center (GRC) has developed a method for fabricating low-density, flexible aerogel composites for use as thermal insulation for myriad applications. It is ideal for a variety of environments that require insulation materials that can withstand temperatures of up to 1200 °C. This innovation significantly advances the state of the art for composite insulation systems, reducing adherence problems and thermal conductivity limitations of conventional aerogel insulations while improving performance with lower weight, lower density, and higher efficiency, all factors contributing to greater applicability of aerogel insulation.

A micrograph of aluminosilicate aerogel shows pore size and distribution.

GRC’s aluminosilicate aerogel composites are fabricated using a sol-gel technique. A sol is formed by hydrolyzing an alumina dispersion in acid solution; the alumina may be combined with a silicon precursor to create a sol.

Fabrics, papers, and felts are used as reinforcing fibers to form an aerogel composite. The aerogel adheres to the reinforcement without use of sizing or organic binders. (In the case of sized fabrics, the sizing is first removed by heat cleaning.) Composites can be fabricated in a batch process, impregnating individual layers of paper, felt, or fabric with the precursor sol, or in a roll-to-roll process. The sol is allowed to gel, and then aged for several days prior to supercritical drying using liquid CO2. Heat treatment of the super critically dried composites can be used to tailor the alumina or aluminosilicate crystal structure and pore size.

In contrast to commercially available insulations, GRC’s innovation provides extremely low thermal conductivity (60 mW/m-K at 900 °C in argon) at high temperatures, thus enabling use at higher temperatures and improving applicability. In addition, GRC’s unique process provides very good adhesion of the aerogel to its reinforcing fibers in alumina papers and zirconia felts, eliminating the spalling seen in other aerogel composites. Finally, GRC’s innovation demonstrates low density and extreme resilience to high temperatures and harsh conditions. Seven layers of composite material of 1.25 mm/layer produced a temperature drop of 700 °C when tested in the 8-foot high-temperature wind tunnel (8 HTT) at NASA’s Langley Research Center. The technology also has withstood heat tests of up to 1200 °C. In combination with other insulators, it has withstood fluxes of up to 65 W/cm2, producing a temperature drop of 625 °C across 8 mm.

The technology has applications in numerous environments requiring insulation in high temperatures, including insulation for thermal protection systems (TPSs), inflatable decelerators, heat shields, fire blankets, oil and gas industry applications, radioisotope power systems, thermoelectrics, and aerospace and aviation systems.

NASA is actively seeking licensees to commercialize this technology. Please contact the Technology Transfer Office at This email address is being protected from spambots. You need JavaScript enabled to view it. to initiate licensing discussions. Follow this link for more information: http://technology.nasa.gov/patent/TB2016/TOP3-413.

The U.S. Government does not endorse any commercial product, process, or activity identified on this web site.