This invention is a manufacturing process of a high-temperature, ceramics-based composite material that features excellent heat and oxidation resistance and frictional properties. The composite material is a dense SiC-infiltrated composite material, a dense carbon-fiber-reinforced SiC-infiltrated composite material, or a dense SiC-infiltrated composite material with granular carbon dispersed. The material is made by infiltrating molten carbon-silicide of Mo or a eutectic mixture of carbon-silicide and silicon carbide into a silicon-carbide-based preform, and then cooling and solidifying the melt.

The material has such a high oxidation resistance that it can be used in the atmosphere at 1,300 °C. or higher. Accordingly, this material can be used for areas that require high heat resistance and high mechanical strength and reliability, or where the target product may have a complicated shape.

Get the complete report on this technology at:
www.techbriefs.com/tow/201010b.html
Email: This email address is being protected from spambots. You need JavaScript enabled to view it.
Phone: 781-972-0600

The U.S. Government does not endorse any commercial product, process, or activity identified on this web site.