Materials & Coatings

Making Single-Source Precursors of Ternary Semiconductors

Commercially available reagents are used in a simplified synthesis.

&A synthesis route has been developed for the commercial manufacture of single- source precursors of chalcopyrite semiconductor absorber layers of thin-film solar photovoltaic cells. The semiconductors in question are denoted by the general formula CuInxGa1–xSySe2–y, where 0≤x≤1 and 0≤y≤1.

Posted in: Briefs, Materials, Semiconductors

Water-Free Proton-Conducting Membranes for Fuel Cells

Fuel cells could be operated at higher temperatures for greater efficiency.

Poly-4 -vinylpyridinebisulfate (P4VPBS) is a polymeric salt that has shown promise as a water-free proton-conducting material (solid electrolyte) suitable for use in membrane/electrode assemblies in fuel cells. Heretofore, proton-conducting membranes in fuel cells have been made from perfluorinated ionomers that cannot conduct protons in the absence of water and, consequently, cannot function at temperatures >100 °C. In addition, the stability of perfluorinated ionomers at temperatures >100 °C is questionable. However, the performances of fuel cells of the power systems of which they are parts could be improved if operating temperatures could be raised above 140 °C. What is needed to make this possible is a solidelectrolyte material, such as P4VPBS, that can be cast into membranes and that both retains proton conductivity and remains stable in the desired higher operating temperature range.

Posted in: Briefs, TSP, Materials, Fuel cells, Conductivity, Electrolytes, Polymers

Removing Bioactive Contaminants by Use of Atomic Oxygen

Bioactive contaminants are removed without using liquid chemical baths or high temperatures.

A method of removing endotoxins and other biologically active organic compounds from the surfaces of solid objects is based on exposure of the objects to monatomic oxygen generated in oxygen plasmas. The mon- atomic oxygen reacts strongly and preferentially with the organic contaminants to form volatile chemical species. The method was developed especially for removing such contaminants as lipopolysaccharides, proteins, lipids, and other biologically active contaminants from surfaces of orthopedic implants prior to sterilization and implantation; if not removed, these con- taminants can contribute to inflammation that sometimes necessitates the surgical removal of the implants.

Posted in: Briefs, TSP, Materials

Glass/BNNT Composite for Sealing Solid Oxide Fuel Cells

Boron nitride nanotubes contribute to strength and fracture toughness.

A material consisting of a barium calcium aluminosilicate glass reinforced with 4 weight percent of boron nitride nanotubes (BNNTs) has shown promise for use as a sealant in planar solid oxide fuel cells (SOFCs). The composition of the glass in question in mole percentages is 35BaO + 15CaO + 5Al2O3 + 10B2O3 + 35SiO2. The glass was formulated to have physical and chemical properties suitable for use as a planar- SOFC sealant, but has been found to be deficient in one aspect: it is susceptible to cracking during thermal cycling of the fuel cells. The goal in formulating the glass/BNNT composite material was to (1) retain the physical and chemical advantages that led to the prior selection of the barium calcium aluminosilicate glass as the sealant while (2) increasing strength and fracture toughness so as to reduce the tendency toward cracking.

Posted in: Briefs, TSP, Materials, Fuel cells, Composite materials, Glass, Nanomaterials

Improved Single-Source Precursors for Solar-Cell Absorbers

Deposition properties and final compositions can be tailored.

Improved single-source precursor compounds have been invented for use in spray chemical vapor deposition (spray CVD) of chalcopyrite semiconductor absorber layers of thin-film solar photovoltaic cells. The semiconductors in question are denoted by the general formula CuInxGa1–xSySe2–y, where x≤1 and y≤2. These semiconductors have been investigated intensively for use in solar cells because they exhibit longterm stability and a high degree of tolerance of radiation, and their bandgaps correlate well with the maximum photon power density in the solar spectrum. In addition, through selection of the proportions of Ga versus In and S versus Se, the bandgap of CuInxGa1–xSySe2–y can be tailored to a value between 1.0 and 2.4 eV, thus making it possible to fabricate cells containing high and/or graded bandgaps.

Posted in: Briefs, TSP, Materials, Solar energy, Semiconductors

Spray CVD for Making Solar-Cell Absorber Layers

Spray CVD combines the advantages of metalorganic CVD and spray pyrolysis.

Spray chemical vapor deposition (spray CVD) processes of a special type have been investigated for use in making CuInS2 absorber layers of thin-film solar photovoltaic cells from either of two subclasses of precursor compounds:
[(PBu3) 2Cu(SEt)2In(SEt)2] or [(PPh3)2Cu(SEt)2 In(SEt)2] . CuInS2 is a member of the class of chalcopyrite semiconductors described in the immediately preceding article. [(PBu3)2Cu(SEt)2In(SEt)2] and [(PPh3)2 Cu(SEt)2In(SEt)2] are members of the class of single-source precursors also described in the preceding article.

Posted in: Briefs, TSP, Materials, Solar energy, Spraying, Chemicals, Gases

Making Ternary Quantum Dots From Single-Source Precursors

Relative to a prior process, this process is simpler and safer.

A process has been devised for making ternary (specifically, CuInS2) nanocrystals for use as quantum dots (QDs) in a contemplated next generation of highefficiency solar photovoltaic cells. The process parameters can be chosen to tailor the sizes (and, thus, the absorption and emission spectra) of the QDs.

Posted in: Briefs, TSP, Materials, Solar energy, Product development, Fabrication, Refractory materials

Increasing Durability of Flame-Sprayed Strain Gauges

Low-oxygen heat treatments and internal platinum oxygen-diffusion barriers extend lifetimes.

Thermally sprayed dielectric ceramic coatings are the primary means of attaching strain and temperature gauges to hot-section rotating parts of turbine engines. As hot-section temperatures increase, lifetimes of installed gauges decrease, and seldom exceed one hour above 2,000 °F ( ≈1,100 °C). Advanced engine components are expected to operate at temperatures approaching 2,200 °F ( ≈1,200 °C), and the required high-temperature lifetime is 10 hours minimum.

Posted in: Briefs, Materials, Ceramics, Coatings Colorants and Finishes, Coatings, colorants, and finishes, Gas turbines, Test equipment and instrumentation

Multifunctional, High-Temperature Nanocomposites

Electrical and thermal conductivities increase with proportions of nanotubes.

In experiments conducted as part of a continuing effort to incorporate multifunctionality into advanced composite materials, blends of multi-walled carbon nanotubes and a resin denoted “PETI-330” (wherein “PETI” is an abbreviation for “phenylethynyl- terminated imide”) were prepared, characterized, and fabricated into moldings. PETI-330 was selected as the matrix resin in these experiments because of its low melt viscosity (<10 poise at a temperature of 280 °C), excellent melt stability (lifetime >2 hours at 280 °C), and high temperature performance (>1,000 hours at 288 °C). The multi-walled carbon nanotubes (MWCNTs), obtained from the University of Kentucky, were selected because of their electrical and thermal conductivity and their small diameters. The purpose of these experiments was to determine the combination of thermal, electrical, and mechanical properties achievable while still maintaining melt processability.

Posted in: Briefs, TSP, Materials, Product development, Molding, Composite materials, Conductivity, Nanomaterials, Resins

Multilayer Impregnated Fibrous Thermal Insulation Tiles

Temperature rises are limited by transpiration cooling.

The term “secondary polymer layered impregnated tile” (“SPLIT”) denotes a type of ablative composite-material thermal- insulation tiles having engineered, spatially non-uniform compositions. The term “secondary” refers to the fact that each tile contains at least two polymer layers wherein endothermic reactions absorb considerable amounts of heat, thereby helping to prevent overheating of an underlying structure. These tiles were invented to afford lighter-weight alternatives to the reusable thermal-insulation materials heretofore variously used or considered for use in protecting the space shuttles and other spacecraft from intense atmospheric- entry heating. Tiles of this type could also be useful on Earth as relatively lightweight components of fire-retardant structures.

Posted in: Briefs, TSP, Materials, Composite materials, Insulation, Polymers, Lightweighting, Rescue and emergency vehicles and equipment, Spacecraft