A process for hydroxide-assisted bonding has been developed as a means of joining optical components made of ultra-low-expansion (ULE) glass, while maintaining sufficiently precise alignment between. The process is intended mainly for use in applications in which (1) bonding of glass optical components by use of epoxy does not enable attainment of the required accuracy and dimensional stability and (2) conventional optical contacting (which affords the required accuracy and stability) does not afford adequate bond strength.
The first and most critical phase of the present hydroxide-assisted-bonding process is the preparation of the surfaces to be bonded. This phase includes the following steps:
1. Ultrasonic cleaning in successive baths of acetone, methanol, and propanol, using an ultrasound cleaner that operates at several Megahertz (Megasonics).
2. Treatment in a solution of potassium hydroxide and ammonium hydroxide in an ultrasonic cleaner, at Megahertz frequencies.
Thorough rinsing with deionized water is carried out after each of the above-mentioned steps. The last rinse is followed by ultrasonic cleaning in deionized water, then the cleaned surfaces are blow-dried with ionized air.
After preparation of the surfaces as described above, a droplet of a dilute solution of potassium hydroxide is placed on one of the surfaces, then the surfaces are placed in contact and gently squeezed together (see figure). The resulting assembly is allowed to sit at room temperature for 24 hours, and is then baked at a temperature of 200 °C for 24 hours. In mechanical tests, sample bonds made by this process were found to have tensile strengths of at least 1.3 kpsi (≈9 MPa), where the epoxy bond used to attach the sample to the tensile stress test apparatus broke.
This work was done by Alexander Abramovici and Victor White of Caltech for NASA's Jet Propulsion Laboratory. For more information, contact
NPO-45247