There are many ways to coat an optic and optimize the coating for a specific application, some more interesting than others. But any thin film coating process requires raw materials, coating capabilities, deposition chamber(s), coating software, a spectrophotometer, and an efficient production system that can produce the desired coating or effect while keeping within the customer’s requisite specifications. This article will focus on the challenge of customizing a non-polarizing cube beamsplitter for a 3D visual application and detail the steps taken to make this challenge a reality.
It was an interesting and intriguing challenge when a customer recently inquired about fabrication of a broadband, non-polarizing cube beamsplitter for a 3D visual app. The client wanted a beamsplitter with a 50% reflection (R) and 50% transmission (T) that would be optimized to operate at wavelengths between 425 nm and 675 nm at 48 degrees, plus or minus 6 degrees. They also wanted both S & P within 10 percent over 48 degrees, plus or minus 6 degrees angle of incidence (AOI).
This is a complex request for several reasons. To start with, a broadband, nonpolarizing beamsplitter (NPBS) is difficult to make. Most non-polarizing beamsplitters are only made at 45 degrees. It’s complicated when trying to achieve the 48 degrees because the change in S & P shift starts to increase rapidly after 45 degrees. Furthermore, most non-polarizing beamsplitters are made for a single wavelength. For example, a 632.8 nm beamsplitter might be used for specific applications, such as holographic and 3D tasks.
To successfully manufacture a broadband NPBS, you need to have extremely precise material calibration as well as good process repeatability. This is done by doing periodic calibration runs on all of the materials to verify that all the refractive indexes, ratios, and tool factors are accurate. Making a 50/50 R/T non-polarizing beamsplitter is also tricky because there is a small amount of metal in the coating that can cause absorption. In this case, the customer’s expectation of a 50/50 split was not something that could be promised. So it was important to explain to the customer that the NPBS would be 48/48. Since that ratio was acceptable to the customer, the project could proceed.
Another issue, which is important for color control, is getting the polarization flat across the wavelength range of 425 nm – 675 nm. If the polarization is not uniform, the color uniformity will be compromised. Additionally, since the customer wanted the AOI to be 48 degrees, plus or minus 6 degrees, the 12 degree change in the angle of incidence created some obstacles. All these factors affect the angle of incidence. Successfully achieving all these benchmarks in order to meet customer specifications – i.e. the 50/50, the polarization flat across the wavelength range, and the change in the AOI – made this project particularly challenging.
Using the TFCalc™ coatings software program, which provides for the design and manufacture of precision optical thin film coatings, different material combinations were selected to design this non-polarizing beamsplitter. The following section details the steps that were taken to reach a satisfactory and very successful thin film optical coating for the customer.
The Challenge – Step by Step
When this project began, the first spec was a 50/50 cube beamsplitter design using tantalum oxide (Ta2O5) silicon dioxide (SiO2) (Figure 1 - Ta2O5/SiO2). These materials were selected to achieve the 50/50 beamsplitter reflection/transmission ratio. When the customer decided that they needed the prism to be non-polarizing, other design options needed to be considered. To accommodate the non-polarizing specification, one material was changed to titanium dioxide (TiO2) paired with the SiO2 and a small amount of metal. In the next graph (Figure 2 - TiO2/SiO2), it is clear that at 45 degrees, the polarization looks good.