Poly-4 -vinylpyridinebisulfate (P4VPBS) is a polymeric salt that has shown promise as a water-free proton-conducting material (solid electrolyte) suitable for use in membrane/electrode assemblies in fuel cells. Heretofore, proton-conducting membranes in fuel cells have been made from perfluorinated ionomers that cannot conduct protons in the absence of water and, consequently, cannot function at temperatures >100 °C. In addition, the stability of perfluorinated ionomers at temperatures >100 °C is questionable. However, the performances of fuel cells of the power systems of which they are parts could be improved if operating temperatures could be raised above 140 °C. What is needed to make this possible is a solid electrolyte material, such as P4VPBS, that can be cast into membranes and that both retains proton conductivity and remains stable in the desired higher operating temperature range.

A family of solid-electrolyte materials different from P4VPBS was described in "Anhydrous Proton-Conducting Membranes for Fuel Cells" (NPO-30493), NASA Tech Briefs, Vol. 29, No. 8 (August 2005), page 48. Those materials notably include polymeric quaternized amine salts. If molecules of such a polymeric salt could be endowed with flexible chain structures, it would be possible to overcome the deficiencies of simple organic amine salts that must melt before being able to conduct protons. However, no polymeric quaternized amine salts have yet shown to be useful in this respect.

The present solid electrolyte is made by quaternizing the linear polymer poly- 4-vinylpyridine (P4VP) to obtain P4VPBS. It is important to start with P4VP having a molecular weight of 160,000 daltons because P4VPBS made from lower-molecular-weight P4VP yields brittle membranes.

In an experimental synthesis, P4VP was dissolved in methanol and then reacted with an excess of sulfuric acid to precipitate P4VPBS. The precipitate was recovered, washed several times with methanol to remove traces of acid, and dried to a white granular solid.

In another synthesis, nanoparticles of silica rich with surface hydroxyl groups were added to P4VP in methanol solution, which was then reacted with excess sulfuric acid to precipitate granules of a composite that most probably had the composition (P4VPBS)–SiO2–SiO(HSO4)2.

The granular P4VPBS produced in the first-mentioned synthesis was dissolved in water to make a gluelike, turbid solution; the granular P4VPBS/silica composite produced in the second-mentioned synthesis was mixed with water to make a turbid, gluelike suspension. The proportions of polymer salt to water in such preparations can be varied; it was found that approximately equal parts of water and polymer salt yield a solution or suspension amenable to further processing.

Each of these preparations was brushed onto an open mat of glass fibers. The coated mats were dried in flowing air at a temperature of 60 °C for about an hour. The coated mats were further dried in a vacuum oven at 60 °C to remove traces of water.

The thermal stability of P4VPBS was evaluated by differential scanning calorimetry. The results showed that P4VPBS undergoes a glass transition at a temperature of about 182 °C and that it melts at about 298.7 °C, with no evidence of decomposition. These thermal properties are consistent with the requirements for stability under operating conditions in fuel cells.

Cell Potential vs. Current Density was measured in a test of an experimental membrane/electrode assembly in a hydrogen/oxygen fuel cell at a temperature of 183.5 °C.

The coated mats were tested to determine their ionic conductivities and to quantify their performances as membranes in hydrogen/oxygen fuel cells. The ionic conductivity of the mat coated with the P4VPBS/silica composite was slightly greater than that of the mat coated with P4VPBS: this was expected because the composite contains additional molecular groups that are presumably available for forming hydrogen bonds. On the basis of the observed temperature dependence of the conductivity, the activation energy for conduction was estimated to be about 0.1 eV, suggesting hopping-type conduction through hydrogen bonds. While the measured conductivity values were two orders of magnitude lower than desirable for fuel cell applications, the degree of solid-state proton conduction was the highest observed thus far in polymeric salts. It is anticipated that the polymer backbone could be modified to facilitate formation of hydrogen bonds to obtain more sites for proton hopping and, hence, greater proton conductivity.

In preparation for the tests of fuel-cell performance, the coated mats were further coated with catalytic anode and cathode layers to form membrane/electrode assemblies. No attempt was made to optimize the catalytic layers. In the fuel-cell tests, stable maximum cell potentials of 0.85 V were attained. The anticipated maximum cell voltage was 1.0 V. The decrease from the expected maximum value was attributed to some crossover of hydrogen and oxygen through the membranes. The figure shows some of the data from the fuel-cell test of the mat coated with the P4VPBS/silica composite. The power density indicated by these data is low for a fuel cell operating at the indicated temperature — presumably because of the lack of optimization of the catalyst layers. Nevertheless, the data suggest that optimization of catalysts and enhancement of conductivity should make it possible to realize high-temperature fuel cells.

This work was done by Sekharipuram Narayanan and Shiao-Pin Yen of Caltech for NASA's Jet Propulsion Laboratory. For more information, download the Technical Support Package (free white paper) at www.techbriefs.com/tsp under the Materials category.

In accordance with Public Law 96-517, the contractor has elected to retain title to this invention. Inquiries concerning rights for its commercial use should be addressed to:

Innovative Technology Assets Management
JPL
Mail Stop 202-233
4800 Oak Grove Drive
Pasadena, CA 91109-8099
(818) 354-2240
E-mail: This email address is being protected from spambots. You need JavaScript enabled to view it.

Refer to NPO-30873, volume and number of this NASA Tech Briefs issue, and the page number.



This Brief includes a Technical Support Package (TSP).
Document cover
Water-Free Proton-Conducting Membranes for Fuel Cells

(reference NPO-30873) is currently available for download from the TSP library.

Don't have an account? Sign up here.