A process for fabricating thermoelectric modules with vacuum gaps separating the thermoelectric legs has been conceived, and the feasibility of some essential parts of the process has been demonstrated. The vacuum gaps are needed to electrically insulate the legs from each other. The process involves the use of scaffolding in the form of sheets of a polymer to temporarily separate the legs by the desired distance, which is typically about 0.5 mm. During a bonding subprocess that would take place in a partial vacuum at an elevated temperature, the polymer would be vaporized, thereby creating the vacuum gaps. If desired, the gaps could later be filled with an aerogel for thermal insulation and to suppress sublimation of thermoelectric material, as described in “Aerogels for Thermal Insulation of Thermoelectric Devices” (NPO-40630), NASA Tech Briefs, Vol. 30, No. 7 (July, 2006), page 50.
A simple thermoelectric module would typically include thermoelectric legs stacked perpendicularly between metal contact pads on two ceramic substrates (see figure). As the design of the thermoelectric module and the fabrication process are now envisioned, the metal contact pads on the ceramic substrates would be coated with a suitable bonding metal (most likely, titanium), and the thermoelectric legs would be terminated in a possibly different bonding metal (most likely, molybdenum). Prior to stacking of the thermoelectric pads between the metal pads on the ceramic substrates, the polymer sheets would be bonded to the appropriate sides of the thermoelectric legs. After stacking, the resulting sandwich structure would be subjected to uniaxial pressure during heating in a partial vacuum to a temperature greater than 700 °C. The heating would bond the metal pads on the legs to the metal pads on the substrates and would vaporize the polymer sheets. The uniaxial pressure would hold the legs in place until bonding and vaporization were complete.
Ideally, the polymer chosen for use in this process should be sufficiently rigid to enforce dimensional stability of the gaps and should vaporize at a temperature low enough that it does not undergo pyrolysis. (Pyrolysis would create an undesired electrically conductive carbonaceous residue.) Poly(a-methylstyrene) [PAMS] has been selected as a promising candidate. PAMS is considered to be rigid, and, in a partial vacuum of 10–6 torr (˜1.3 × 10–4 Pa), it vaporizes in the temperature range of 250 to 400 °C, without pyrolizing.
Initially, the primary concern raised by vaporization of polymer scaffolding was that polymer-vapor residue might interfere with the bonding of the thermoelectric legs to the metal pads on the ceramic substrates. In an experiment to investigate the likelihood of such interference, a mockup comprising two molybdenum legs separated by a PAMS sheet in contact with a titanium plate was placed under uniaxial pressure and heated to a temperature of 950 °C in a partial vacuum of 10–6 torr. Strong, uniform bonds were made between the molybdenum legs and the titanium plate, demonstrating that the PAMS vapor did not interfere with bonding.
This work was done by Jeffrey Sakamoto, Shiao-pin Yen, Jean-Pierre Fleurial, and Jong- Ah Paik of Caltech for NASA’s Jet Propulsion Laboratory. For further information, access the Technical Support Package (TSP) free on-line at www.techbriefs.com/ tsp under the Materials category.
In accordance with Public Law 96-517, the contractor has elected to retain title to this invention. Inquiries concerning rights for its commercial use should be addressed to:
Innovative Technology Assets Management
JPL Mail Stop
202-233 4800 Oak Grove Drive
Pasadena, CA 91109-8099
Refer to NPO-41248 volume and number of this NASA Tech Briefs issue, and the page number.
This Brief includes a Technical Support Package (TSP).
Vaporizable Scaffolds for Fabricating Thermoelectric Modules
(reference NPO-41248) is currently available for download from the TSP library.
Don't have an account? Sign up here.