NASA PS400 is a solid lubricant coating invented for high-temperature tribological applications. This plasma-sprayed coating is a variant of the previously patented PS304 coating, and has been formulated to provide higher density, smoother surface finish, and better dimensional stability.

This innovation is a new composite material that provides a means to reduce friction and wear in mechanical components. PS400 is a blend of a nickel-molybdenum binder, chrome oxide hardener, silver lubricant, and barium fluoride/calcium fluoride eutectic lubricant that can either be sprayed or deposited by other means, such as powder metallurgy. The resulting composite material is then finished by grinding and polishing to produce a smooth, selflubricating surface.

This work was done by Christopher DellaCorte and Brian J. Edmonds of Glenn Research Center. For more information, download the Technical Support Package (free white paper) at under the Materials category.

Inquiries concerning rights for the commercial use of this invention should be addressed to

NASA Glenn Research Center
Innovative Partnerships Office
Attn: Steven Fedor
Mail Stop 4–8
21000 Brookpark Road
Ohio 44135.

Refer to LEW-18561-1.